Thermal shock is a type of rapidly transient mechanical load. By definition, it is a mechanical load caused by a rapid change of temperature of a certain point. It can be also extended to the case of a thermal gradient, which makes different parts of an object expand by different amounts. This differential expansion can be more directly understood in terms of strain, than in terms of stress, as it is shown in the following. At some point, this stress can exceed the tensile strength of the material, causing a crack to form. If nothing stops this crack from propagating through the material, it will cause the object's structure to fail.
Failure due to thermal shock can be prevented by:
- Reducing the thermal gradient seen by the object, by changing its temperature more slowly or increasing the material's thermal conductivity
- Reducing the material's coefficient of thermal expansion
- Increasing its strength
- Introducing built-in compressive stress, as for example in tempered glass
- Decreasing its Young's modulus
- Increasing its toughness, by crack tip blunting (i.e., plasticity or phase transformation) or crack deflection
Effect on materials
Borosilicate glass is made to withstand thermal shock better than most other glass through a combination of reduced expansion coefficient and greater strength, though fused quartz outperforms it in both these respects. Some glass-ceramic materials (mostly in the (LAS) system) include a controlled proportion of material with a negative expansion coefficient, so that the overall coefficient can be reduced to almost exactly zero over a reasonably wide range of temperatures.
Reinforced carbon-carbon is extremely resistant to thermal shock, due to graphite's extremely high thermal conductivity and low expansion coefficient, the high strength of carbon fiber, and a reasonable ability to deflect cracks within the structure.
To measure thermal shock, the impulse excitation technique proved to be a useful tool. It can be used to measure Young's modulus, Shear modulus, Poisson's ratio and damping coefficient in a non destructive way. The same test-piece can be measured after different thermal shock cycles and this way the deterioration in physical properties can be mapped out.
Thermal shock resistance
Thermal shock resistance measures can be used for material selection in applications subject to rapid temperature changes. A common measure of thermal shock resistance is the maximum temperature differential, , which can be sustained by the material for a given thickness.
Strength-controlled thermal shock resistance
Thermal shock resistance measures can be used for material selection in applications subject to rapid temperature changes. The maximum temperature jump, , sustainable by a material can be defined for strength-controlled models by:
may be approximated by:
Perfect heat transfer
- for cold shock in plates
- for hot shock in plates
A material index for material selection according to thermal shock resistance in the fracture stress derived perfect heat transfer case is therefore:
Poor heat transfer
- for cold shock
- for hot shock
In the poor heat transfer case, a higher heat transfer coefficient is beneficial for thermal shock resistance. The material index for the poor heat transfer case is often taken as:
According to both the perfect and poor heat transfer models, larger temperature differentials can be tolerated for hot shock than for cold shock.
Fracture toughness controlled thermal shock resistance
In addition to thermal shock resistance defined by material fracture strength, models have also been defined within the fracture mechanics framework. Lu and Fleck produced criteria for thermal shock cracking based on fracture toughness controlled cracking. The models were based on thermal shock in ceramics (generally brittle materials). Assuming an infinite plate and mode I cracking, the crack was predicted to start from the edge for cold shock, but the center of the plate for hot shock. Cases were divided into perfect and poor heat transfer to further simplify the models.
Perfect heat transfer
The sustainable temperature jump decreases, with increasing convective heat transfer (and therefore larger Biot number). This is represented in the model shown below for perfect heat transfer ().
- for cold shock
- for hot shock
A material index for material selection in the fracture mechanics derived perfect heat transfer case is therefore:
Poor heat transfer
Critically, for poor heat transfer cases, materials with higher thermal conductivity, k, have higher thermal shock resistance. As a result a commonly chosen material index for thermal shock resistance in the poor heat transfer case is:
Kingery thermal shock methods
The formulas were derived for ceramic materials, and make the assumptions of a homogeneous body with material properties independent of temperature, but can be well applied to other brittle materials.
Thermal shock testing exposes products to alternating low and high temperatures to accelerate failures caused by temperature cycles or thermal shocks during normal use. The transition between temperature extremes occurs very rapidly, greater than 15 °C per minute.
Equipment with single or multiple chambers is typically used to perform thermal shock testing. When using single chamber thermal shock equipment, the products remain in one chamber and the chamber air temperature is rapidly cooled and heated. Some equipment uses separate hot and cold chambers with an elevator mechanism that transports the products between two or more chambers.
Glass containers can be sensitive to sudden changes in temperature. One method of testing involves rapid movement from cold to hot water baths, and back.
Examples of thermal shock failure
- Hard rocks containing ore veins such as quartzite were formerly broken down using fire-setting, which involved heating the rock face with a wood fire, then quenching with water to induce crack growth. It is described by Diodorus Siculus in Egyptian gold mines, Pliny the Elder, and Georg Agricola.
- Ice cubes placed in a glass of warm water crack by thermal shock as the exterior surface increases in temperature much faster than the interior. The outer layer expands as it warms, while the interior remains largely unchanged. This rapid change in volume between different layers creates stresses in the ice that build until the force exceeds the strength of the ice, and a crack forms, sometimes with enough force to shoot ice shards out of the container.
- Incandescent bulbs that have been running for a while have a very hot surface. Splashing cold water on them can cause the glass to shatter due to thermal shock, and the bulb to implode.
- An antique cast iron cookstove is a simple iron box on legs, with a cast iron top. A wood or coal fire is built inside the box and food is cooked on the top outer surface of the box, like a griddle. If a fire is built too hot, and then the stove is cooled by pouring water on the top surface, it will crack due to thermal shock.
- It is widely hypothesized [by whom?] that following the casting of the Liberty Bell, it was allowed to cool too quickly which weakened the integrity of the bell and resulted in a large crack along the side of it the first time it was rung. Similarly, the strong gradient of temperature (due to the dousing of a fire with water) is believed to cause the breakage of the third Tsar Bell.
- Thermal shock is a primary contributor to head gasket failure in internal combustion engines.
- Askeland, Donald R. (January 2015). "22-4 Thermal Shock". The science and engineering of materials. Wright, Wendelin J. (Seventh ed.). Boston, MA. pp. 792–793. ISBN 978-1-305-07676-1. OCLC 903959750.
- US Patent 6066585, "Ceramics having negative coefficient of thermal expansion, method of making such ceramics, and parts made from such ceramics", issued 2000-05-23, assigned to Emerson Electric Co.
- Ashby, M. F. (1999). Materials selection in mechanical design (2nd ed.). Oxford, OX: Butterworth-Heinemann. ISBN 0-7506-4357-9. OCLC 49708474.
- Soboyejo, Wole O. (2003). "12.10.2 Materials Selection for Thermal Shock Resistance". Mechanical properties of engineered materials. Marcel Dekker. ISBN 0-8247-8900-8. OCLC 300921090.
- T. J. Lu; N. A. Fleck (1998). "The Thermal Shock Resistance of Solids" (PDF). Acta Materialia. 46 (13): 4755–4768. doi:10.1016/S1359-6454(98)00127-X.
- KINGERY, W. D. (Jan 1955). "Factors Affecting Thermal Stress Resistance of Ceramic Materials". Journal of the American Ceramic Society. 38 (1): 3–15. doi:10.1111/j.1151-2916.1955.tb14545.x. ISSN 0002-7820.
- Soboyejo, Wole O. (2003). "12.10 Thermal Shock Response". Mechanical properties of engineered materials. Marcel Dekker. ISBN 0-8247-8900-8. OCLC 300921090.
- ASTM C149 — Standard Test Method for Thermal Shock Resistance of Glass Containers